OBTAINING OF WEAR-RESISTANT COATINGS ON DETAILS OF VEHICLES UNDER NON-STATIO-NARY TEMPERATURE CONDITIONS

O. O. Beygul, S. I. Adamchuk, D. B. Sereda, A. S. Shulga

Abstract


In this work, we consider the production of protective coatings on the details of the crank mechanism. Steel 50 was used for the research. The coating was formed for 15-60 minutes at a temperature of 900-10500С. The optimum compositions of SHS-charge containing 10% B, 7% Si, 20% Ti were obtained. It is established that with increa-sing hardness wear resistance increases. On the surface, a micro hardness of 15000-17500 MPa was obtained. Due to alloying of chromium-coating coatings with boron, silicon and titanium, obtaining an increase in wear resistance by 1.8-2.1 times than for coatings obtained under isothermal conditions and the term of chemical-thermal treatment decreased by 2.5-4 times. This allows you to reduce energy costs during the process of chemical-thermal treatment.

Keywords


wear resistance; synthesis; steel; micro hardness; phase

References


Лахтин Ю.М. Химико-термическая обработка металлов / Ю.М.Лахтин, Б.Н.Арза-масов // М.: Металлургия, 1985. – 256с.

Лахтин Ю.М. Металловедение и термическая обработка металлов / Лахтин Ю.М. // М.: Металлургия, 1994. – 494с.

Сыркин В.Г. СVD-метод. Химическое парофазное осаждение / Сыркин В.Г. // М.: Наука, 2000. – 496с.

Химико-термическая обработка металлов и сплавов: справочник / [Борисенок Г.В., Васильев Л.А., Ворошнин Л.Г. и др.]. // М.: Металлургия, 1981. – 424с.

Sereda B. Obtaining of Boride Coatings under SHS Conditions for Car Parts / Sereda D., Sereda B. // Material science and technology-2016. – Salt Lake City, Utah USA, 2016. – 1339p. – P.945-948.

Sereda B. Development of Protective Coatings Formulations Based on Boron for Units Operating at High Temperatures in Metallurgy / Sereda D., Sereda B. // Material science and technology-2016. – Salt Lake City, Utah USA, 2016. – 1339p. – P.931-934.

Sereda B. Corrosion Resistance and Mechanical Properties Zinc Coating Sheet Steels, Received in Conditions of Self-propagating High Temperature Synthesis / Sereda D., Sereda B. // Material science and technology-2016. – Salt Lake City, Utah USA, 2016. – 1339p. – P.825-829.

Лахтин Ю.М. Поверхностное упрочнение сталей и сплавов / Ю.М.Лахтин // Металловедение и термическая обработка металлов. – 1988. – № 11. – С.14-25.

Коган Я.Д. Перспективы развития технологий поверхностного упрочнения материалов деталей машин и инструмента / Я.Д.Коган // Металловедение и термическая обработка металлов. – 1993. – № 8. – С.5-9.

Ворошнин Л.Г. Борирование промышленных сталей и чугунов: справочное пособие / Ворошнин Л.Г. – Мн.: Беларусь, 1981. – 205с.

Середа Б.П. Поверхневе зміцнення матеріалів: монографія / Середа Б.П., Калініна Н.Є., Кругляк І.В. – Запоріжжя: РВВ ЗДІА, – 2004. – 230с.

Мержанов А.Г. Твердо-пламенное горение / Мержанов А.Г. – Черноголовка: ИСМАН, 2000. – 244с.

СВС дисперсных алюминидов никеля и защитные покрытия на их основе / Б.М.Вольпе, В.В.Евтстигнеев, И.В.Милюков [и др.] // Физика и химия обраб. материалов. – 1996. – №1. – С.50-54.

СВС дисперсных материалов Ti-Al и защитные покрытия на их основе / Б.М.Вольпе, В.В.Евтстигнеев, И.В.Милюков [и др.] // Физика и химия обраб. материалов. – 1995. – №2. – С.73-79.


Refbacks

  • There are currently no refbacks.


Copyright (c) 2018 Collection of scholarly papers of Dniprovsk State Technical University (Technical Sciences)

ISSN (print) 2519-2884

ISSN (online) 2617-8389